Cable Cover Plate

Excavation and the digging of trenches could post danger and hazard to workers. It can also cause severe and costly damages to underground Electrical Cables, Telecommunication Optical Fiber Cable Networks and Gas Distribution System, Industrial and also the Domestic Water Piping System.

These have led to the development of the Warning Marker Plate. Manufactured from Polyvinyl Chloride, LITAFLEX uPVC Cable Cover Plate possesses high impact strength and complies with the International Standard.

Its superior quality deem excellent for the protection of Cables and Pipes installed underground. For example, the wide range of bright, luminous colours with embosses raised lettering, will certainly enable easy identification, and thereby effectively signal caution when digging trenches. In addition, the ingenious design of the Interlocking Device also allows continuous connection.

covers



Flat Plate
Product no.
Dimension ( mm )
A
B
Pallet
PCS
M3
PF 120 120 1.8 2000 0.75
PF 150 150 2.0 2000 1.00
PF 200 200 2.0 1600 1.20

STANDARD LENGTH :  1 Meter
COLOUR :  Yellow / Black
 
 




Standard Embossing
DANGER bijli LT CABLE
DANGER bijli HT CABLE
 1-dia


Angle Plate
Product no.
Dimension ( mm )
A
B
Pallet
PCS
M3
PA 120 120 1.8 2000 0.90
PA 150 150 2.0 2000 1.00
PA 172 172 2.0 1000 1.11
PA 272 272 2.0 1000 1.11

STANDARD LENGTH :  1 Meter
COLOUR :  Yellow / Black
 
 
 2-dia


Flat Smooth Plate
Product no.
Dimension ( mm )
A
B
Pallet
PCS
M3
PS 200 200 2.0 25 1.64

STANDARD LENGTH :  50 Meter Coil
COLOUR :  Yellow / Black
 
 
 3-dia



Chartacteristics Result
ASTM D1525 : 2007
Standard Test Method for Vicat Softening Temperature of Plastics
Load  (1kgf)
Heat Transfer Medium  (Silicone Oil)
Heating Rate (50 +/- 5oC/hr)
Vicat Softening Point, average



88oC
ONORM E6530 (CLAUSE 7.3) : 1985
Impact Strength (Drop Hammer Test)

Maximum Depth of Penetration of the 10kg drop Hammer
Observation
< 100mm
: No crack
Characteristics Result
ONORM E6530 (Clause 7.4) : 1985
Tensile Load of the longitudinal Connection
Crosshead Speed (50mm/ min)
Average Tensile Load prior to ageing
Average Tensile Load after ageing
Change in Tensile Load
:1056N
:1071N
:1.4%
Conditioning of Test Specimen
ASTM D3045 : 1997
Practice for Heat Ageing of Plastics without Load
Oven Temperature (70 + 2oC)
Duration (168 hr)